| Particle Size | 2.2-2.6mm |
|---|---|
| Specific Surface Area | ≥850 M2/g |
| Purity | ≥99% |
| Carrier Material | Alumina |
| Boiling Point | Not Available |
| Pore Volume | 0.6-0.8 Cm3/g |
|---|---|
| Na2O Content | ≤0.2% |
| Surface Area | 100-110 M2/g |
| Crystalline Phase | Q-Al2O3 |
| Moisture Content | ≤1% |
| Materiał nośnika | Glinka |
|---|---|
| Application | Catalyst For 2-ethylanthraquinone Hydrogenation |
| Specific Surface Area | ≥850 M2/g |
| Boiling Point | Not Available |
| Purity | ≥99% |
| Kolor | Biały |
|---|---|
| Crushing Strength | ≥80N |
| Cao Content | ≤0.05% |
| Chemical Composition | Al2O3 ≥ 97% |
| Size | 1-5mm |
| Zawartość MgO | ≤0,05% |
|---|---|
| Zawartość wilgoci | ≤1% |
| Wymiar | biały proszek |
| Zawartość Cao | ≤0,05% |
| Zawartość SiO2 | ≤0,05% |
| Faza krystaliczna | Q-Al2O3 |
|---|---|
| Powierzchnia | 100-110 m2/g |
| Stabilność termiczna | Do 1200℃ |
| Rozmiar cząsteczki | 1,6-1,8 mm |
| Zawartość Na2O | ≤0,2% |
| Rozmiar cząsteczki | 2,2-2,6 mm |
|---|---|
| Przechowywanie | Przechowywać w suchym miejscu |
| Materiał nośnika | Glinka |
| Czystość | ≥99% |
| Zastosowanie | Katalizator do uwodornienia 2-etyloantrachinonu |
| Zawartość MgO | ≤0,05% |
|---|---|
| Powierzchnia | 100-110 m2/g |
| Wymiar | biały proszek |
| Gęstość nasypowa | 0,6-0,65 g/cm3 |
| Zawartość Fe2O3 | ≤0,02% |
| Objętość porów | 0,6-0,8 cm3/g |
|---|---|
| Wzór chemiczny | Al2O3 |
| Zawartość SiO2 | ≤0,05% |
| Stabilność termiczna | Do 1200℃ |
| Zawartość Cao | ≤0,05% |
| Specyficzna powierzchnia | ≥850 m2/g |
|---|---|
| Przechowywanie | Przechowywać w suchym miejscu |
| Temperatura wrzenia | Nie jest dostępny |
| Rozmiar cząsteczki | 2,2-2,6 mm |
| Materiał nośnika | Glinka |